Название: Microstructure, mechanical properties and machining performance of hot-pressed Al[2]O[3]-ZrO[2]-TiC composites
Авторы: Grigoriev, Mikhail Vladimirovich
Kotelnikov, N.
Buyakova, Svetlana Petrovna
Kulkov, Sergey Nikolaevich
Ключевые слова: микроструктуры; механические свойства; механическая обработка; производительность; горячее прессование; композиты; композиционные материалы
Дата публикации: 2016
Издатель: IOP Publishing
Библиографическое описание: Microstructure, mechanical properties and machining performance of hot-pressed Al[2]O[3]-ZrO[2]-TiC composites / M. V. Grigoriev [et al.] // IOP Conference Series: Materials Science and Engineering. — 2016. — Vol. 116 : Advanced Materials and New Technologies in Modern Materials Science : International Conference, 9–11 November 2015, Tomsk, Russia : [proceedings]. — [012002, 5 p.].
Аннотация: The effect of adding nanocrystalline ZrO[2] and submicron TiC to ultrafine Al[2]O[3] on mechanical properties and the microstructure of the composites developed by hot pressing was investigated. It was shown that by means of hot pressing in an argon atmosphere at a sintering temperature of 1500 °С one can obtain the composites Al[2]O[3] - ZrO[2] - TiC with a fine structure and minimal porosity. It has been shown that in material a multi-scale hierarchical structure is formed, which possesses high physical and mechanical properties: the hardness and fracture toughness was 21.5 GPa and 5.2 MPa*m{1/2} respectively, the modulus of elasticity was 500 GPa and bending strength was 390 MPa. Tests on composites' cutting properties were carried out on interrupted cutting of hardened steel. All samples had wear of the cutting edge in the form of chips of the grain rear working surface of the tool, but the cutting tool which was made by Al2O3 - 10% ZrO2 - 10% TiC had a minimum width of wear.
URI: http://earchive.tpu.ru/handle/11683/18934
Располагается в коллекциях:Материалы конференций

Файлы этого ресурса:
Файл РазмерФормат 
dx.doi.org-10.1088-1757-899X-116-1-012002.pdf1,19 MBAdobe PDFПросмотреть/Открыть


Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.