Title: Исследование возможностей повышения рабочих температур ферритно-мартенситной стали ЭК-181 с помощью высокотемпературной термомеханической обработки
Other Titles: The study of the possibilities of the operating temperatures of ferriticmartensitic steel EK-181 increasing by high temperature thermomechanical treatment
Authors: Алмаева, К. В.
Полехина, Н. А.
metadata.dc.contributor.advisor: Литовченко, И. Ю.
Keywords: температура; стали; высокотемпературная обработка; термомеханическая обработка; жаропрочные стали; прочность; пластические свойства; охрупчивание
Issue Date: 2018
Publisher: Издательский Дом Томского государственного университета
Citation: Алмаева К. В. Исследование возможностей повышения рабочих температур ферритно-мартенситной стали ЭК-181 с помощью высокотемпературной термомеханической обработки / К. В. Алмаева, Н. А. Полехина ; науч. рук. И. Ю. Литовченко // Перспективы развития фундаментальных наук : сборник научных трудов XV Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 24-27 апреля 2018 г. : в 7 т. — Томск : Издательский Дом Томского государственного университета, 2018. — Т. 1 : Физика. — [С. 39-41].
Abstract: High-temperature (T=650-800°С) mechanical properties of ferritic-martensitic steel EK-181 after traditional heat treatment (normalized and tempered, N&T) and high-temperature thermomechanical treatment (HTMT) were studied. It is shown that at high test temperatures HTMT leads to an increase in the strength properties of the steel relative to N&T. At tension temperature Т=720 °С the yield strength of the steel after HTMT is higher than the corresponding values after N&T at a temperature Т = 650 °С. The studies of the microstructure of steel after HTMT have shown that such treatment leads to an increase in the dislocation density and in dispersion and volume fraction of nanoscale particles of vanadium carbonitride V (C, N). Such particles are capable to provide thermal stability of a microstructure and enhanced values of long-term hightemperature strength of the steel. This modification of the structural and phase state of the steel can provide an increase in the expected operating temperatures.
URI: http://earchive.tpu.ru/handle/11683/50740
Appears in Collections:Материалы конференций

Files in This Item:
File SizeFormat 
conference_tpu-2018-C21_V1_p39-41.pdf193 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.