Title: Electrochemical hydrogenation after mechanical activated near equiatomic Ti-Ni powder
Authors: Abdulmenova, E.
Vaulina, Olga Yurievna
Kulkov, Sergey Nikolaevich
Keywords: гидрирование; механическая активация; порошки; шаровые мельницы; стехиометрия
Issue Date: 2019
Publisher: IOP Publishing
Citation: Abdulmenova E. Electrochemical hydrogenation after mechanical activated near equiatomic Ti-Ni powder / E. Abdulmenova, O. Yu. Vaulina, S. N. Kulkov // IOP Conference Series: Materials Science and Engineering. — Bristol : IOP Publishing, 2019. — Vol. 511 : Perspective Materials of Constructional and Medical Purpose : International Scientific and Technical Youth Conference, 26–30 November 2018, Tomsk, Russian Federation : [proceedings]. — [012009, 5 p.].
Abstract: It has been studied an effect of mechanical activation in a planetary ball milling on the electrochemical hydrogenation of Ti-Ni powder near equiatomic content. It has been shown that average particle sizes measured by scanning electron microscope decreased from 11.1 to 7.8 [mu]m up to 30 s mechanical activation, then increased to 33.2 [mu]m for 300 s activation. Beside, with an increase in the time of mechanical activation was formed state with small the coherently diffracting domain which correspond to quasi-amorphous state of material. It has been shown that after hydrogenation, the particle size distribution did not change. There is an incubation time hydrogenation for mechanical activation, when hydrogenation is not occurring. Mechanical activation for more than 30 s leads to the formation of the Ti[2]NiHx phase based on the Ti[2]Ni and 50 s activation is sufficient to form the Ti[2]NiH[0.5] stoichiometry. For a longer mechanical activation a phase with the stoichiometry Ti[2]NiH[0.85] was formed and to obtain the Ti[2]NiH stoichiometry it is necessary to carry out activation for 4.5 hours.
URI: http://earchive.tpu.ru/handle/11683/55441
Appears in Collections:Материалы конференций

Files in This Item:
File SizeFormat 
dx.doi.org-10.1088-1757-899X-511-1-012009.pdf1,03 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.