Structural-phase state and mechanical properties of submicrocrystalline titanium alloy Ti-6Al-4V obtained with use of reversible hydrogen alloying

Abstract

Features of evolution of structural-phase state of titanium alloy Ti-6Al-4V at the process of submicrocrystalline structure formation using reversible hydrogen alloying have been investigated by methods of electron microscopic and X-ray diffraction analyses. Influence of hydrogen alloying on mechanical properties at stretching of submicrocrystalline titanium alloy Ti-6Al-4V in temperature interval of 293...1023 K was studied. Possible reasons of increase in ultimate and yield strength and reduction of deformation to destruction of submicrocrystalline alloy Ti-6Al-4V in temperature interval 873...1023 K at hydrogen alloying in quantity 0,08...0,33 mas. % were discussed