Formation and Characterization of Crystalline Hydroxyapatite Coating with the (002) Texture

Abstract

This study reports the effect of titanium (Ti) microstructure on the mechanical properties and surface wettability of thin (<800 nm) hydroxyapatite (HA) coating deposited via radio-frequency (RF) magnetron sputtering. It was revealed that the sand-blasting (SB) and acid etching (AE) of Ti prior deposition led to a wide range of surface roughness in nano/micro scale. After nanostructured HA coating deposition such physico-mechanical characteristics as nanohardness H, Young's modulus E, H/E ratio and H[3]/E[2] were significantly improved. Moreover, HA coatings exhibited improved wear resistance, lower friction coefficient and ability of the coating to wetting.