Исследование смачиваемости углеродных компонентов полиуретановым связующим резистивных композитов

Abstract

The research paper deals with influence wettability of carbon components with the polyurethane binder of resistive composites. We have revealed that the polyurethane lacquer wets up to 25 wt. % of C-1 and GE-3 particles, which results in their uniform distribution over the entire volume of the binder and homogeneity of RCMs. Zero wetting of the same weight percentage is observed in the case of K-163 carbon black, which gives rise to caking and distortion of homogeneity of the composite coating after its formation and its further cracking after heat treatment. The wetting capacity of K-163 carbon black in the polyurethane lacquer is improved using a DISPERBYK-2155 dispersing agent in the amount of 10 wt. % with respect to the binder. The resulting experimental data indicate that C-1 particles exhibit the best wettability, hence their adhesion strength with the binder would be higher than that of GE-3 graphite element and K-163 carbon black.