Название: | Microstructural Analysis of Novel Preceramic Paper-Derived SiCf/SiC Composites |
Авторы: | Li Ke Kashkarov, Egor Borisovich Ma Hailiang Fan Ping Zhang Qi Zhang Peng Zhang Jilong Wu Zhaouhui Wahl Larissa Laptev, Roman Sergeevich Lider, Andrey Markovich Travitsky (Travitzky), Nakhum Travitsky (Travitzky), Nakhum Yuan Daqing |
Ключевые слова: | композиты; карбид кремния; микроструктуры; аннигиляция; позитроны; laminated composite; silicon carbide; microstructures; positron annihilation |
Дата публикации: | 2021 |
Издатель: | MDPI AG |
Библиографическое описание: | Microstructural Analysis of Novel Preceramic Paper-Derived SiCf/SiC Composites / Li Ke, E. B. Kashkarov, Ma Hailiang [et al.] // Materials. — 2021. — Vol. 14, iss. 22. — [6737, 13 p.]. |
Аннотация: | This paper presents the results of microstructural analysis of novel preceramic paper-derived SiCf/SiC composites fabricated by spark plasma sintering. The sintering temperature and pressure were 2100/2200 °C and 60/100 MPa, respectively. The content of fibers in the composites was approx. 10 wt %. The SiCf/SiC composites were analyzed by positron annihilation methods, X-ray diffraction technology, scanning electron microscopy, and Raman spectroscopy. Longer sintering time causes the proportion of the 6H-SiC composition to increase to ~80%. The increase in sintering temperature from 2100 °C to 2200 °C leads to partial transition of 4H-SiC to 6H-SiC during the sintering process, and the long-life component of positrons indicates the formation of Si vacancies. The Raman characteristic peaks of turbostratic graphite appear in the Raman spectrum of SiC fibers, this is caused by the diffusion of carbon from the surface of the SiC fiber and the preceramic paper during the high-temperature sintering process. |
URI: | http://earchive.tpu.ru/handle/11683/72766 |
Располагается в коллекциях: | Репринты научных публикаций |
Файлы этого ресурса:
Файл | Описание | Размер | Формат | |
---|---|---|---|---|
reprint-nw-37639.pdf | 1,16 MB | Adobe PDF | Просмотреть/Открыть |
Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.