High-Temperature Steam Oxidation of Accident-Tolerant Cr/Mo-Coated Zr Alloy at 1200–1400 °C

Abstract

The oxidation resistance under LOCA conditions of bilayer Cr/Mo coating deposited on Zr-1Nb zirconium alloy was investigated in this paper. The bilayer Cr (8 ?m)/Mo (3 ?m) coatings were deposited by magnetron sputtering. Then, oxidation resistance under high-temperature oxidation at 1200–1400 °C in a water steam was studied. The use of a Mo sublayer resulted in limiting Cr-Zr interdiffusion under high-temperature oxidation. It was shown that the Mo barrier sublayer (~3 ?m) can provide the protective behavior of the Cr/Mo-coated Zr at 1330 °C in a water steam for at least 720 s. The weight gain of the bilayer Cr/Mo samples was comparable with the monolayer Cr samples after oxidation at 1400 °C. In addition, the analysis of the Cr/Mo-coated Zr alloy oxidation behavior at 1400 °C was carried out.