Title: | Mechanical and tribological characteristics of a-C:H:SiOx films formed by PACVD on titanium alloy VT1-0 |
Authors: | Grenadyorov, A. S. Solovyev, A. A. Oskomov, K. V. Yaroslavtseva, O. A. |
Keywords: | механические характеристики; триботехнические характеристики; пленки; титановые сплавы; плазмохимическое осаждение; импульсные напряжения; шероховатости; поверхности |
Issue Date: | 2019 |
Publisher: | IOP Publishing |
Citation: | Mechanical and tribological characteristics of a-C:H:SiOx films formed by PACVD on titanium alloy VT1-0 / A. S. Grenadyorov [et al.] // IOP Conference Series: Materials Science and Engineering. — Bristol : IOP Publishing, 2019. — Vol. 511 : Perspective Materials of Constructional and Medical Purpose : International Scientific and Technical Youth Conference, 26–30 November 2018, Tomsk, Russian Federation : [proceedings]. — [012019, 7 p.]. |
Abstract: | This paper is devoted to the study of the mechanical and tribological properties of aC:H:SiOx films deposited on a titanium alloy VT1-0 by a plasma chemical deposition method using pulsed bipolar bias voltage. It was shown that after deposition of 2 [mu]m-thick a-C:H:SiOx film on a titanium alloy VT1-0 sample, the root-mean-square surface roughness Rq measured using atomic force microscopy decreased from 74 to 50 nm compared to the original substrate. The surface hardness H measured using nanoindentation increased from 3.3 to 12.4 GPa with an almost unchanged elasticity modulus E. As a result, the plasticity index (H/E) of titanium samples increased from 0.03 to 0.11, and the plastic deformation resistance (H3/E2 ) increased from 3 to 156 MPa. Deposition of a-C:H:SiOx film on the titanium alloy VT1-0 surface makes possible to reduce the friction coefficient from 0.3-0.6 to 0.1 and the wear rate from 6·10-4 to 7•10{-6} mm{3} /Nm. |
URI: | http://earchive.tpu.ru/handle/11683/55432 |
Appears in Collections: | Материалы конференций |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
dx.doi.org-10.1088-1757-899X-511-1-012019.pdf | 829,45 kB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.