Electro-explosive alloying of VT6 alloy surface by boron carbide powder with the subsequent electron-beam treatment

Abstract

The formation of electro-explosive alloying zone with the thickness up to 50 µm has been revealed. It has been shown that it has a gradient structure, characterized by the decrease of carbon and boron concentration with the increase of the distance up to the treatment surface. The subsequent electron-beam treatment of alloying zone leads to flattening of alloying surface relief and is accompanied by the formation of a multilevel structure at the depth up to 30 µm, characterized by the interchange of some layers with a different level of alloying, having structure of a submicro- and nanoscale level.