Название: Effect of Metal Additives on the Combustion Characteristics of High-Energy Materials
Авторы: Korotkikh, Aleksandr Gennadievich
Glotov, Oleg
Sorokin, Ivan
Ключевые слова: добавки; металлы; сжигание; высокоэнергетические материалы; горение; порошки; твердые топлива; алюминиевые порошки; дисперсность
Дата публикации: 2016
Издатель: [s. n.]
Библиографическое описание: Korotkikh A. G. Effect of Metal Additives on the Combustion Characteristics of High-Energy Materials / A. G. Korotkikh, O. Glotov, I. Sorokin // MATEC Web of Conferences. — 2016. — Vol. 72 : Heat and Mass Transfer in the System of Thermal Modes of Energy – Technical and Technological Equipment (HMTTSC-2016) : April 19-21, 2016, Tomsk, Russia : [proceedings]. — [01048, 6 p.].
Аннотация: Thermodynamic calculation of combustion parameters and equilibrium composition of HEMs combustion products showed, that at the increase of aluminum powder dispersity the specific impulse and combustion temperature of solid propellants are reduced due to the decrease of the mass fraction of active aluminum in particles. Partial or complete replacement of aluminum by metal powder (B, Mg, AlB[2], Al\Mg alloy, Fe, Ti and Zr) in HEMs composition leads to the reduce of the specific impulse and combustion temperature. Replacement of aluminum powder by boron and magnesium in HEM reduces the mass fraction of condensed products in the combustion chamber of solid rocket motor. So, for compositions HEMs with boron and aluminum boride the mass fraction in chamber is reduced by 24 and 36 %, respectively, with respect to the composition HEMs with Al powder. But the mass fraction of CCPs in the nozzle exit increases by 13 % for HEMs with aluminum boride due to the formation of boron oxide in the condensed combustion products. Partial replacement of 2 wt. % aluminum powder by iron and copper additives in HEM leads to the reduce of CCPs mass fraction in chamber by 4–10 % depending on the aluminum powder dispersity duo to these metals are not formed condensed products at the HEMs combustion in chamber.
URI: http://earchive.tpu.ru/handle/11683/33445
Располагается в коллекциях:Материалы конференций

Файлы этого ресурса:
Файл РазмерФормат 
dx.doi.org-10.1051-matecconf-20167201048.pdf109,27 kBAdobe PDFПросмотреть/Открыть


Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.