Effect of the Compaction Pressure and Ni Content on the Modified Aluminum-Based Perovskite Synthesis Designed to Immobilize the Radioactive Waste in Combustion Mode

Abstract

The article deals with the synthesis of perovskite-like ceramics matrix material for immobilization of radioactive waste by SHS method. The dependence of the compaction pressure on the synthesis of the samples was established. Synthesis conditions for the matrix with the desired properties of the composition were determined that is acceptable for reliable isolation of radionuclides throughout the long-term storage of waste. The maximum amount of aluminum perovskite is observed when the initial mixture compaction pressure equal to 30 MPa and 25% wt. Nickel.