Sintering oxide ceramics based on AI[2]O[3] and ZrO[2], activated by MgO, TiO[2] and SiO[2] additives

Abstract

The positive effect of the addition of MgO and TiO[2] in an amount of no more than 1 wt. % on sintering and physico-mechanical properties of alumina ceramics is established. Addition of 5% of SiO[2] to A1[2]O[3] provides the mechanism of liquid phase sintering of ceramics, which leads to increase in its density and strength up to 480 MPa. In ceramic system A1[2]O[3] - ZrO[2] - Y[2]O[3] highest level of physical and mechanical properties of the composition had a hypereutectic composition 16.6% A1[2]O[3] - 76% Z1O[2] - 7.4% Y[2]O[3]. In this composition two mechanisms of hardening are realized simultaneously, such as transformational hardening by t-m -ZrO[2] transition and dispersion strengthening with high-modulus particles of [alpha]- A1[2]O[3].