Название: | Effect of Proton Irradiation on the Defect Evolution of Zr/Nb Nanoscale Multilayers |
Авторы: | Laptev, Roman Sergeevich Lomygin, Anton Krotkevich, Dmitry Syrtanov, Maksim Sergeevich Kashkarov, Egor Borisovich Bordulev, Yuri Sergeevich Siemek, Krzysztof Kobets, Andrey Gennadjevich |
Ключевые слова: | многослойные покрытия; протонные излучения; спектроскопия; микроструктура; дефекты; nanoscale multilayer coating; Zr/Nb; proton irradiation; positron annihilation spectroscopy; XRD; GD-OES; microstructure; defects |
Дата публикации: | 2020 |
Издатель: | MDPI AG |
Библиографическое описание: | Effect of Proton Irradiation on the Defect Evolution of Zr/Nb Nanoscale Multilayers / R. S. Laptev, A. Lomygin, D. Krotkevich [et al.] // Metals. — 2020. — Vol. 10, iss. 4. — [535, 12 p.]. |
Аннотация: | Nanoscale multilayer coatings (NMCs) with different crystal structures are considered as capable of self-healing after radiation damage due to the recombination of vacancies and interstitials. This work is focused on a defect distribution study of NMCs based on Zr/Nb layers (25/25 nm and 100/100 nm) after proton irradiation. Coatings with a total thickness of 1.05 ± 0.05 µm were irradiated by 900-keV protons using a pelletron-type electrostatic accelerator with an ion current of 2 µA for durations of 60 min to 120 min. The influence of the irradiation effect was studied by X-ray diffraction analysis (XRD), glow discharge optical emission spectrometry (GD–OES), and Doppler broadening spectroscopy using a variable energy positron beam. The results obtained by these methods are compatible and indicate that defect concentration of Zr/Nb NMCs remains unchanged or slightly decreases with increasing irradiation time. |
URI: | http://earchive.tpu.ru/handle/11683/64870 |
Располагается в коллекциях: | Репринты научных публикаций |
Файлы этого ресурса:
Файл | Описание | Размер | Формат | |
---|---|---|---|---|
reprint-nw-33284.pdf | 5,26 MB | Adobe PDF | Просмотреть/Открыть |
Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.