Название: Plastic strain arrangement in copper single crystals in sliding
Авторы: Chumaevsky, Andrey Valerjevich
Tarasov, Sergei Yulievich
Lychagin, Dmitry Vasilievich
Ключевые слова: деформации; монокристаллы; медь; трение; поликристаллические материалы; пластические деформации; оптическая микроскопия; сканирующая электронная микроскопия
Дата публикации: 2014
Издатель: AIP Publishing
Библиографическое описание: Chumaevsky A. V. Plastic strain arrangement in copper single crystals in sliding / A. V. Chumaevsky, S. Yu. Tarasov, D. V. Lychagin // AIP Conference Proceedings. — 2014. — Vol. 1623 : International Conference on Physical Mesomechanics of Multilevel Systems 2014, Tomsk, Russia, 3–5 September 2014 : [proceedings]. — [P. 91-94].
Аннотация: Deformation of tribologically loaded contact zone is one of the wear mechanisms in spite of the fact that no mass loss may occur during this process. Generation of optimal crystallographic orientations of the grains in a polycrystalline materials (texturing) may cause hardening and reducing the deformation wear. To reveal the orientation dependence of an individual gain and simplify the task we use copper single crystals with the orientations of the compression axis along [11 1] and [110]. The plastic deformation was investigated by means of optical, scanning electron microscopy and EBSD techniques. It was established that at least four different zones were generated in the course of sliding test, such as non-deformed base metal, plastic deformation layer sliding, crystalline lattice reorientation layer and subsurface grain structure layer. The maximum plastic strain penetration depth was observed on [110]-single crystals. The minimum stability of [11 1]-crystals with respect to rotation deformation mode as well as activation of shear in the sliding contact plane provide for rotation deformation localization below the worn surface. The high-rate accumulation of misorientations and less strain penetration depth was observed on [11 1]-crystals as compared to those of [110]-oriented ones.
URI: http://earchive.tpu.ru/handle/11683/35726
Располагается в коллекциях:Материалы конференций

Файлы этого ресурса:
Файл РазмерФормат 
dx.doi.org-10.1063-1.4898890.pdf2,48 MBAdobe PDFПросмотреть/Открыть


Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.