Название: Phase composition in NiTi near-surface layers after electron beam treatment and its variation depending on beam energy density
Авторы: Ostapenko, Marina Gennadievna
Meisner, Ludmila
Lotkov, Aleksandr
Gudimova, Ekaterina
Ключевые слова: фазовый состав; слои; электронные пучки; энергия; поверхностные слои
Дата публикации: 2014
Издатель: AIP Publishing
Библиографическое описание: Phase composition in NiTi near-surface layers after electron beam treatment and its variation depending on beam energy density / M. G. Ostapenko [et al.] // AIP Conference Proceedings. — 2014. — Vol. 1623 : International Conference on Physical Mesomechanics of Multilevel Systems 2014, Tomsk, Russia, 3–5 September 2014 : [proceedings]. — [P. 451-454].
Аннотация: In the work, we study the mechanisms of structural phase state formation in NiTi surface layers after low-energy pulsed electron beam irradiation depending on the electron beam energy density. It is revealed that after electron beam treatment of the NiTi specimens at energy densities E[1]=15 J/cm{2}, E[2]=20 J/cm{2}, and E[3]=30 J/cm{2}, a series of effects is observed: the absence of the Ti[2]Ni phase and the presence of new peaks correspond to the B19 martensite phase with monoclinic structure. Estimation of the relative volume content of the B2 and B19 phases from the total intensity of their peaks shows that the percentage of the martensite phase increases from ~5 vol.% in the NiTi specimen irradiated at E[1]=15 J/cm{2} to ~80 vol.% in the NiTi specimen irradiated at E[3]=30 J/cm{2}. It is found that in the NiTi specimens irradiated at E<=20 J/cm{2}, the layer that contains a martensite phase resides not on the surface but at some depth from it.
URI: http://earchive.tpu.ru/handle/11683/35736
Располагается в коллекциях:Материалы конференций

Файлы этого ресурса:
Файл РазмерФормат 
dx.doi.org-10.1063-1.4898979.pdf558,95 kBAdobe PDFПросмотреть/Открыть


Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.