Название: Formation of high-carbon abrasion-resistant surface layers when high-energy heating by high-frequency currents
Авторы: Plotnikova, N. V.
Skeeba, V. Yu.
Martyushev, Nikita Vladimirovich
Miller, R. A.
Rubtsova, N. S.
Ключевые слова: поверхностные слои; углерод; высокая энергия; стали; математическое моделирование; высокочастотные токи; низкоуглеродистые стали
Дата публикации: 2016
Издатель: IOP Publishing
Библиографическое описание: Formation of high-carbon abrasion-resistant surface layers when high-energy heating by high-frequency currents / N. V. Plotnikova [et al.] // IOP Conference Series: Materials Science and Engineering. — 2016. — Vol. 156 : Materials and Technologies of New Generations in Modern Materials Science : International Conference and Youth Scientific School, 9–11 June 2016, Tomsk, Russia : [proceedings]. — [012022, 5 p.].
Аннотация: The paper shows the possibility of carburization of low-carbon steel surface layers using high-frequency currents. The mathematical modeling of carburization using high-energy heating by high-frequency currents (HEH HFC) has been carried out, the temperature fields formed during the given processing have been calculated, as well as the structural changes in the surface layers have been simulated. The features of the structure formation in the surface layers of low-carbon steel after carburizing via HEH HFC have been determined by optical and scanning microscopy, which is confirmed by the computational models. The rational mode of fusion via HEH HFC has also been determined (power density of the source q[s]=(1.5...4.0)•10{8} W m{-2}, (the relative travel speed of parts V[p]=5 ... 100 mm /sec), with forming the compressive retained stresses in the surface layer ([sigma][RS]=-300...-400 MPa).
URI: http://earchive.tpu.ru/handle/11683/36557
Располагается в коллекциях:Материалы конференций

Файлы этого ресурса:
Файл РазмерФормат 
dx.doi.org-10.1088-1757-899X-156-1-012022.pdf1,2 MBAdobe PDFПросмотреть/Открыть


Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.