Title: Hydrogen Interaction with Deep Surface Modified Zr-1Nb Alloy by High Intensity Ti Ion Implantation
Authors: Kashkarov, Egor Borisovich
Ryabchikov, Aleksandr Ilyich
Kurochkin, Aleksandr Viktorovich
Syrtanov, Maksim Sergeevich
Shevelev, Aleksey Eduardovich
Obrosov, Aleksey
Weifs, Sabine
Keywords: сплавы; цирконий; титан; имплантация; водород; микроструктура; морфология; мартенситная фаза
Issue Date: 2018
Publisher: Томский политехнический университет
Citation: Hydrogen Interaction with Deep Surface Modified Zr-1Nb Alloy by High Intensity Ti Ion Implantation / E. B. Kashkarov [et al.] // Metals. — 2018. — Vol. 8, iss. 12. — [1881, 13 p.].
Abstract: A deep surface modified TiZr layer was fabricated by high-intensity low-energy titanium ion implantation into zirconium alloy Zr-1Nb. Gas-phase hydrogenation was performed to evaluate protective properties of the modified layer against hydrogen permeation into Zr-1Nb alloy. The effects of ion implantation and hydrogen on microstructure, phase composition and elemental distribution of TiZr layer were analyzed by scanning electron microscopy, X-ray diffraction, and glow-discharge optical emission spectroscopy, respectively. It was revealed that TiZr layer (~10 μm thickness) is represented by α′ + α(TiZr) lamellar microstructure with gradient distribution of Ti through the layer depth. It was shown that the formation of TiZr layer provides significant reduction of hydrogen uptake by zirconium alloy at 400 and 500 °C. Hydrogenation of the modified layer leads to refinement of lamellar plates and formation of more homogenous microstructure. Hydrogen desorption from Ti-implanted Zr-1Nb alloy was analyzed by thermal desorption spectroscopy. Hydrogen interaction with the surface modified TiZr layer, as well as its resistance properties, are discussed.
Appears in Collections:Препринты научных публикаций

Files in This Item:
File SizeFormat 
reprint-nw-27984.pdf2,94 MBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.