Название: Hydrogen Interaction with Deep Surface Modified Zr-1Nb Alloy by High Intensity Ti Ion Implantation
Авторы: Kashkarov, Egor Borisovich
Ryabchikov, Aleksandr Ilyich
Kurochkin, Aleksandr Viktorovich
Syrtanov, Maksim Sergeevich
Shevelev, Aleksey Eduardovich
Obrosov, Aleksey
Weifs, Sabine
Ключевые слова: сплавы; цирконий; титан; имплантация; водород; микроструктура; морфология; мартенситная фаза
Дата публикации: 2018
Издатель: Томский политехнический университет
Библиографическое описание: Hydrogen Interaction with Deep Surface Modified Zr-1Nb Alloy by High Intensity Ti Ion Implantation / E. B. Kashkarov [et al.] // Metals. — 2018. — Vol. 8, iss. 12. — [1881, 13 p.].
Аннотация: A deep surface modified TiZr layer was fabricated by high-intensity low-energy titanium ion implantation into zirconium alloy Zr-1Nb. Gas-phase hydrogenation was performed to evaluate protective properties of the modified layer against hydrogen permeation into Zr-1Nb alloy. The effects of ion implantation and hydrogen on microstructure, phase composition and elemental distribution of TiZr layer were analyzed by scanning electron microscopy, X-ray diffraction, and glow-discharge optical emission spectroscopy, respectively. It was revealed that TiZr layer (~10 μm thickness) is represented by α′ + α(TiZr) lamellar microstructure with gradient distribution of Ti through the layer depth. It was shown that the formation of TiZr layer provides significant reduction of hydrogen uptake by zirconium alloy at 400 and 500 °C. Hydrogenation of the modified layer leads to refinement of lamellar plates and formation of more homogenous microstructure. Hydrogen desorption from Ti-implanted Zr-1Nb alloy was analyzed by thermal desorption spectroscopy. Hydrogen interaction with the surface modified TiZr layer, as well as its resistance properties, are discussed.
URI: http://earchive.tpu.ru/handle/11683/57561
Располагается в коллекциях:Препринты научных публикаций

Файлы этого ресурса:
Файл РазмерФормат 
reprint-nw-27984.pdf2,94 MBAdobe PDFПросмотреть/Открыть


Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.